Waya wa Chuma kwa Mfumo wa Magari
| Jina la bidhaa | Waya wa Chuma | Mahali pa asili | Tianjin, Uchina |
| Chapa | MJH | Tumia | Mfumo wa Magari |
Vipimo vya Kufanya Kazi kwa Waya wa Mabati
Kwa kuzingatia kwamba waya wa mabati huainishwa kulingana na kiasi cha mipako ya zinki, jedwali lifuatalo linaonyesha tofauti kati ya nguvu za mkazo.
| Kipenyo cha majina | Idadi ya chini ya bend za nyuma | Idadi ya chini ya Torsions (Bright na Class B) | ||||
| (Bright na Class B) | ||||||
| 1770 MPA | 1960 MPA | 2160Mpa | 1770 MPA | 1960 MPA | 2160Mpa | |
| zaidi ya 0.6mm ~ incl.0.65mm | 11 | 10 | 9 | 28 | 25 | 23 |
| zaidi ya 0.65mm ~ incl.0.70mm | 10 | 9 | 8 | 28 | 25 | 23 |
| zaidi ya 0.70mm ~ incl.0.75mm | 16 | 15 | 14 | 28 | 25 | 23 |
| zaidi ya 0.75mm ~ incl.0.80mm | 15 | 14 | 13 | 28 | 25 | 22 |
| zaidi ya 0.80mm ~ incl.0.85mm | 13 | 12 | 11 | 28 | 25 | 22 |
| zaidi ya 0.85mm ~ incl.0.90mm | 12 | 11 | 10 | 28 | 25 | 22 |
| zaidi ya 0.90mm ~ incl.0.95mm | 11 | 10 | 9 | 28 | 25 | 22 |
| zaidi ya 0.95mm ~ incl.1.00mm | 10 | 9 | 8 | 28 | 25 | 22 |
| zaidi ya 1.00mm ~ incl.1.10mm | 17 | 16 | 14 | 26 | 23 | 21 |
| zaidi ya 1.10mm ~ incl.1.20mm | 16 | 15 | 13 | 26 | 23 | 21 |
| zaidi ya 1.20mm ~ incl.1.30mm | 15 | 14 | 13 | 25 | 22 | 20 |
| zaidi ya 1.30mm ~ incl.1.40mm | 13 | 12 | 10 | 25 | 22 | 19 |
| zaidi ya 1.40mm ~ incl.1.50mm | 11 | 10 | 9 | 25 | 22 | 19 |
| zaidi ya 1.50mm ~ incl.1.60mm | 14 | 13 | 12 | 25 | 22 | 19 |
| zaidi ya 1.60mm ~ incl.1.65mm | 13 | 12 | 11 | 25 | 22 | 19 |
| zaidi ya 1.65mm ~ incl.1.70mm | 13 | 12 | 11 | 25 | 22 | 19 |
| zaidi ya 1.70mm ~ incl.1.80mm | 11 | 11 | 10 | 25 | 22 | 19 |
| zaidi ya 1.80mm ~ pamoja na.1.85mm | 10 | 10 | 8 | 24 | 21 | 18 |
| zaidi ya 1.85mm ~ incl.1.90mm | 10 | 10 | 8 | 24 | 21 | 18 |
| zaidi ya 1.90mm ~ incl.2.00mm | 9 | 9 | 7 | 24 | 21 | 18 |
| Kipenyo cha majina | Uzito wa chini wa mipako (g/m2) | |
| Darasa B | ||
| zaidi ya 0.6mm ~ incl.0.65mm | 60 | |
| zaidi ya 0.65mm ~ incl.0.70mm | 60 | |
| zaidi ya 0.70mm ~ incl.0.75mm | 60 | |
| zaidi ya 0.75mm ~ incl.0.80mm | 60 | |
| zaidi ya 0.80mm ~ incl.0.85mm | 70 | |
| zaidi ya 0.85mm ~ incl.0.90mm | 70 | |
| zaidi ya 0.90mm ~ incl.0.95mm | 70 | |
| zaidi ya 0.95mm ~ incl.1.00mm | 70 | |
| zaidi ya 1.00mm ~ incl.1.10mm | 80 | |
| zaidi ya 1.10mm ~ incl.1.20mm | 80 | |
| zaidi ya 1.20mm ~ incl.1.30mm | 90 | |
| zaidi ya 1.30mm ~ incl.1.40mm | 90 | |
| zaidi ya 1.40mm ~ incl.1.50mm | 100 | |
| zaidi ya 1.50mm ~ incl.1.60mm | 100 | |
| zaidi ya 1.60mm ~ incl.1.65mm | 100 | |
| zaidi ya 1.65mm ~ incl.1.70mm | 100 | |
| zaidi ya 1.70mm ~ incl.1.80mm | 100 | |
| zaidi ya 1.80mm ~ pamoja na.1.85mm | 100 | |
| zaidi ya 1.85mm ~ incl.1.90mm | 115 | |
| zaidi ya 1.90mm ~ incl.2.00mm | 115 |
Sifa za kipenyo
Waya wa Kawaida wa Mabati hutengenezwa ili kuendana na vihimili vifuatavyo vya kipenyo:
| Kipenyo cha Waya cha Jina | Uvumilivu (mm) |
| zaidi ya 0.60mm hadi na incl.1.00mmover 1.00mm hadi na kujumuisha.1.80 mm zaidi ya 1.80mm hadi na incl.2.20 mm | +/-0.015+/-0.02 +/-0.025 |
Kemia ya chuma
Mchanganyiko wa gredi za chuma hutumiwa na michakato ya matibabu ya joto kutengeneza darasa laini, la kati na ngumu.Jedwali hapa chini linaonyesha tu kemia za chuma zinazotumiwa.
| Daraja la Tensile | % Kaboni | % Fosforasi | % Manganese | % Silicone | % Sulfuri |
| Kawaida | 0.45~0.50 | 0.032 | 0.5 ~1.00 | 0.10~0.34 | 0.041 |
| Juu | 0.59~0.63 | 0.035 | 0.5 ~ 1.10 | 0.10~0.35 | 0.045 |
| Ziada-Juu | 0.65~0.83 | 0.035 | 0.5 ~ 1.10 | 0.10~0.35 | 0.045 |
Udhibiti wa Ubora:
Tunatumia mfumo wa udhibiti wa ubora wa jumla.Kila vipande vya malighafi;bidhaa za kumaliza nusu na bidhaa za kumaliza hujaribiwa na kurekodiwa kwenye faili.Rekodi ya ufuatiliaji hutumiwa kutoka kwa bidhaa za mwisho hadi viwanda vya kwanza vya chuma vya malighafi.
Sehemu ya Tatu kama SGS inapatikana kwa udhibiti wa majaribio kabla ya usafirishaji
Ufungashaji:
1) Bidhaa zote zimejaa ufungaji wa baharini.
2) Mahitaji maalum ya Mteja ya kufunga yanaweza kuridhika.
3) Mizigo ya anga;mizigo ya baharini na lori zote zinapatikana.